Product List
- Resin for Surface Treatment
- Adhesive Resin
- Resin for Surface Layer
- Polyurethane Varnish
- Moisture Curing Polyurethane Resin
- Accelerant
- Cross Linking Agent
- Wet Process PU Resin of Moisture and Gas Permeation for Fabric Coating
- Agent and Accelerant
- Dry Process PU Resin for Fabric Coating
- Polyester Polyols
- Water Based Polyurethane Resin for Synthetic Leather
- PU System for Shoe Sole
- Wet Process PU Resin for Synthetic Leather
- Dry Process PU Resin for Adhesive Layer
- Resin for Surface Treatment and Coating
- Dry Process PU Resin
- Wet Process PU Resin
- PU Resin
- Dry Process PU Resin for Fabric Coating
- Wet Process PU Resin for Microfiber
- Common Dry Process PU Resin
English
العرب
PortuguêsWet Process PU Resin for Microfiber
Wet Process PU Resin for Microfiber
Wet-process PU Resin for NaOH Reduction Microfiber
| Name | Viscosity (Pas/25) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-1 | 40~60 | 29.0~31.0 | DMF | 3.0 | 60.0 | 600 | soft grade, hydrolysis resistance, acid resistant, alkali resistant, good dyeing property | NaOH reduction |
| WR-2 | 50~80 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, hydrolysis resistance, acid resistant, alkali resistant, good dyeing property, good resilience | NaOH reduction |
| WR-3 | 40~60 | 29.0~31.0 | DMF | 9.0 | 70.0 | 470 | mid-hard grade, hydrolysis resistance, acid resistant, alkali resistant, good dyeing property | NaOH reduction |
Wet-process PU Resin for TOL Reduction Microfiber
| Name | Viscosity (Pas/25) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-4 | 80~120 | 29.0~31.0 | DMF | 2.0 | 55.0 | 740 | soft grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
| WR-5 | 80~120 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
| WR-6 | 80~120 | 29.0~31.0 | DMF | 9.0 | 65.0 | 650 | mid-hard grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
| WR-7 | 80~120 | 29.0~31.0 | DMF | 15.0 | 60.0 | 500 | hard grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
Wet-process PU Resin for TOL Reduction and Low-cost Microfiber
| Name | Viscosity (Pas/25) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-8 | 160~220 | 29.0~31.0 | DMF | 5.0 | 55.0 | 700 | mid-soft grade, anti-TOL extracting, low-cost type | TOL reduction |
| WR-9 | 80~120 | 29.0~31.0 | DMF | 15.0 | 52.0 | 500 | hard grade, anti-TOL extracting, low-cost type | TOL reduction |
Wet-process PU Resin for TOL Reduction and Good Resilience Microfiber
| Name | Viscosity (Pas/25) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-10 | 80~120 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, anti-TOL extracting, hydrolysis resistance, acid resistant, alkali resistant, good resilience | TOL reduction |
Wet-process PU Resin for TOL Reduction and Thin Shirring Microfiber
| Name | Viscosity (Pas/25) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-11 | 80~120 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, anti-TOL extracting, hydrolysis resistance, acid resistant, alkali resistant, thin shirring | TOL reduction |
| WR-12 | 120~150 | 29.0~31.0 | DMF | 10.0 | 75.0 | 750 | mid-hard grade, anti-TOL extracting, hydrolysis resistance, acid resistant, alkali resistant, thin shirring | TOL reduction |
We area China-based wet process PU resin for microfiber manufacturer. Our company has built up a complete research, manufacture and sales system. We are involved in the production of PU resins including dry process PU resin, wet process PU resin, wet process PU resin for microfiber, water based polyurethane resign for surface layer, etc. Our products are ISO9001 certified. Contact us for the PU resin for microfiber you are looking for. Thank you!
Feedback Form
Other Products
- Dry Process PU Resin for Fabric Coating Dry Process PU Resin for Fabric Coating Dry-process Moisture and Gas Permeation PU ResinNameViscosity (Pas/25)Solid(%)Solvents100% Modulus (MPa)Tensi
- PU Resin PU ResinPU resin is a thermoplastic polymer material that takes on different characteristics when produced with different materials or production met
- Wet Process PU Resin Wet Process PU ResinWet process PU resin is produced by adding DMF solvents and other additives to the raw resin. The obtained mixture is then deaera
- Dry Process PU Resin Dry Process PU ResinDry process PU resin is made by smearing PU resin on release papers with different patterns. It is then dried and adhered with ba
- Resin for Surface Treatment and Coating Resin for Surface Treatment and CoatingResin for surface treatment and coating, as the name suggests, is a resin used on the surface of the base mate