United Kingdom
United States
Argentina
Brazil
China
France
Germany
Japan
Korea
Russia
Spain
Switzerland
Thailand
UAE
Vietnam
Poland
Italy
Morocco
Malaysia
Portugal
India
Canada
- Electric Tool Brushes
- Carbon Holders
- Automotive,Motorcycle Brushes
- Industrial Brushes
- Graphite Plates, Graphite Segments
- Graphite Turbine Rings, Graphite Molds
- Silver Brush, Copper Brushes
- Silicon Carbide-Mechanical Seals
- Highly Purified Graphite
- Hot Pressing Graphite
- Carbon Graphite,Metal Impregnated Graphite
EnglishSilicon Carbide-Mechanical Seals
Silicon Carbide-Mechanical Seals
Specifications of Silicon CarbideMechanical Seals [ Graphite Products ]:
|
| |||||
| Technical Parameters | Unit | ||||
| Bulk Density | g/cm2 | 3.9 | |||
| Rockwell Hardness | HRA | 87 | |||
| Porosity | % | <0.4 | |||
| Coefficient of Thermal Conductivity | W/M.K | 16.7 | |||
| Flexural Strength | g/cm2 | 2800 | |||
|
| ||||||
| Technical Parameters | Unit | Reacting Sintering | Pressureless Sintering | |||
| Shore Hardness | HS | 100 | 105 | |||
| Porosity | % | 0.3 | 0.2 | |||
| Bulk Density | g/cm2 | 3.00 | 3.05 | |||
| Compressive Strength | Mpa | 1150 | 1200 | |||
| Bending Strength | Mpa | 335 | 350 | |||
| Thermal Expansion Coefficient | / | 4.510-4 | 4.510-4 | |||
|
| ||||||
| Technical Parameters | Unit | Reacting Sintering | ||||
| Rockwell Hardness | HRA | 88-91 | ||||
| Porosity | % | 0.2 | ||||
| Bulk Density | g/cm2 | 14.8-15 | ||||
| Bending Strength | Mpa | 1470 | ||||
| Thermal Expansion Coefficient | -6/ | 5.510-6 | ||||
- Silver Brush, Copper Brushes Silver Brush,Copper Brushes
- Graphite Turbine Rings, Graphite Molds Graphite Turbine Rings, Graphite Molds
- Graphite Plates, Graphite Segments Graphite Plates, Graphite Segments
- Industrial Brushes Industrial Brushes
- Automotive,Motorcycle BrushesAutomotive,Motorcycle BrushesSpecifications of Automotive, MotorcycleBrushes [ Graphite Products ] Model Resistivity (m) Shore Hardness