Applications		Type	Type Mix (A+C)/B	Hard- ness (Shore)	Relative Density (g/cm³)		(By Weight) A/B	C/A weight ratio (g/Kg)		Charac- teristics
common man-sole		SM-1	HT-5600 +SM-2 / F-2180	65 ~72A	0.55 ~0.60		100/119 ~119.5	213 5/18		good moldability
Common women-sole			HT-5606 +SM-2 / F-2180	58 ~65A	0.55 ~0.65		100/99 ~101	243 5/18		good moldability
casual shoes		SM-2	HT-5608B +SM-2 / F-2180	60 ~65A	0.46 ~0.55		100/110 ~112	270 5/18		light
		SM-3	HT-8740 +SM-2 / F-2580B	50 ~55A	0.48 ~0.55		100/92 ~93	305 5/18		soft, good feeling
		SM-4	HT-5840 +SM-2 / F-2290	35 ~40A	0.55 ~0.65		100/70.5 ~72.5	310 5/18		soft, good feeling
		SM-5	HT-5650 +SM-2 / F-2290B	55 ~62A	0.44 ~0.52		100/84.5 ~86.5	230 5/18		soft, good feeling
injection shoes	out-sole	SM-6	HT-8801L +SM-2 / F-2580B	70 ~75A	0.80 ~1.10		100/86 ~87	305 5/18		good bondability
	in-sole	SM-7	HT-8801L +(SM-2+H2O) / F-2580B	45 ~50A	0.45 ~0.50		100/92 ~93	305 5/18		good bondability
	out-sole	SM-8	HT-8806 +SM-2 / F-2290	60 ~65A	0.90 ~1.10		100/66.5 ~67.5	280 5/18		high bonding strength
	in-sole	SM-9	HT-8808 +(SM-2+ SM-6) / F-2290	50 ~55A	0.55 ~0.60		100/89 ~91	(300 +60) 5/18		high bonding strength
	out-sole	SM-10	HT-2033 +SM-2 / F-2580	66 ~71A	0.90 ~1.10		100/115 ~116	450 5/17		good bondability, cold resistance
	in-sole	SM-11	HT-2033 +(SM-2+ H2O) / F-2580	45 ~50A	0.40 ~0.45		100/73 ~74	450 5/17		good bondability, cold resistance
high heels shoes		SM-12	HT-5890 +SM-2 / F-2290B	85 ~93A	0.68 ~0.75		100/117.5 ~119.5	250 5/18		high hardness, high support strength
wedge heels shoes		SM-13	HT-5670 +SM-2 / F-2290B	65 ~72A	0.44 ~0.52		100/91 ~93	230 5/18		light, high support strength
wedge heels shoes		SM-14	HT-5560 +SM-2 / F-2290B	60 ~65A	0.42 ~0.48		100/133 ~135	250 5/18		light, high support strength
cold resistance shoes		SM-15	HT-9305 +SM-2 / F-2580	70 ~75A	0.60 ~0.65	100/125.5 ~126			240 5/18	cold resistance, high support strength
		SM-16	HT-2004 +SM-2 / F-2580	57 ~62A	0.60 ~0.65	100 / 94 ~94.5			220 5/18	cold resistance
		SM-17	HT-6510 +SM-2 / F-3682	48 ~52A	0.58 ~0.62	100/64 ~66			480 5/18	polyether type, excellent cold resistance
		SM-18	HT-3065 +SM-7 / F-3220	65 ~70A	0.60 ~0.65	100/99 ~101			340 5/17	polyether type, excellent cold resistance
mid-sole		SM-19	HT-6748B +(DC-332 +SM-66) / F-2290	60 ~68C	0.35 ~0.45	100/60 ~62			(130 +100) 5/18	glabrous surface
insole		SM-20	HT-6730 +(DC-332 +SM-2) / F-2580B	35 ~45C	0.25 ~0.35	100/72.5 ~74.5			(110 +145) 5/18	soft, comfort
insole		SM-21	HT-3033 +SM-2 / F-3240	30 ~40C	0.24 ~0.32	100/65 ~67			50 5/17	polyether type, feeling in low temperature

Note:
1. The PU systems for shoe soles consists of the following: polyol mixture (A), isocyanate compound (B) and catalyst compound (C).
2. Packaging of the PU systems for shoe soles : A compound (polyol mixture) is packed in an 18Kg plastic drum; the B compound (isocyanate compound) is packed in a 20Kg drum; the C compound (catalyst compound) is packed in a 10Kg plastic drum.
3. With the nitrogen seal unbroken, the storage life for B compound (isocyanate compound) is 3 months; the storage life for A compound (polyol admixture) is 6 months. When the storage life expires, the material is still usable if every index stays qualified.

We are leading manufacturer of the PU systems for shoe soles with close to 16 years of experience. With advanced technology and management support, we have the capacity to produce water-based polyurethane resin for synthetic leather, wet process PU resin, dry process PU resin, and more products. All these products are of high quality and offered at low prices. Located in port-city, we can ship our the PU systems for shoe soles at affordable shipping costs.

Feedback Form

Other Products

Water Based Polyurethane Resin for Synthetic Leather Water Based Polyurethane Resin for Synthetic Leather Water based polyurethane resin for synthetic leather is a water-based polyurethane resin exclusi

Polyester Polyols Polyester PolyolsSeriesTypeM.WOH Value mgKOH/gAcid Value mgKOH/gMoisture %Melting Point Color APHAPackage Kg/bucketApplicationsEGYS-1200053.00 ~59.00

Dry Process PU Resin for Fabric Coating Dry Process PU Resin for Fabric Coating Fabric coating is a process of adding coating material to the surface of the fabric. In a broad sense, fabric

Agent and Accelerant Agent and AccelerantIn order to meet different demands of our global clients, we also offer cross linking agents and accelerants.Cross linking agent

Wet Process PU Resin of Moisture and Gas Permeation for Fabric Coating Wet Process PU Resin of Moisture and Gas Permeation for Fabric CoatingNameViscosity (Pas/25)Solid (%)Solvents100% Modulus (MPa)Tensile Strength (MPa)